LEXAN(沙伯基礎)HP2NR/PC(聚碳酸酯)物性表參數
沙伯基礎SABIC塑料LEXAN HP2NR聚碳酸酯（PC）是一種中等流動性原料，MVR（300°C / 1.2kg）為16.這是一種生物相容性（ISO10993或USP VI級），適用于醫療器械應用。 它是EtO可消毒的，不含脫模級。
 |
沙伯基礎SABIC塑料LEXAN HP2NR PC物性表參數PDF文檔下載 |
以下是LEXAN(沙伯基礎)HP2NR/PC(聚碳酸酯)物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 68 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 125 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 2370 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 | |
| Hardness, Rockwell M | 70 | - | ASTM D 785 | |
| Hardness, Rockwell R | 118 | - | ASTM D 785 | |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 | |
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 65 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 694 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | NA | J/m | ASTM D 256 | |
| Tensile Impact Strength, Type S | 546 | kJ/m² | ASTM D 1822 | |
| Falling Dart Impact (D 3029), 23°C | 169 | J | ASTM D 3029 | |
| Instrumented Impact Total Energy, 23°C | 62 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 60 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 10 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 65 | kJ/m² | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m² | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy Impact, notched, 23°C | 35 | kJ/m² | ISO 179/2C | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 154 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 129 | °C | ASTM D 648 | |
| CTE, -40°C to 95°C, flow | 6.84E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 95°C, xflow | 6.84E-05 | 1/°C | ASTM E 831 | |
| Specific Heat | 1.25 | J/g-°C | ASTM C 351 | |
| Thermal Conductivity | 0.19 | W/m-°C | ASTM C177 | |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 | |
| CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 140 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 141 | °C | ISO 306 | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 122 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.2 | - | ASTM D 792 | |
| Specific Volume | 0.83 | cm³/g | ASTM D 792 | |
| Density | 1.19 | g/cm³ | ASTM D 792 | |
| Water Absorption, 24 hours | 0.15 | % | ASTM D 570 | |
| Water Absorption, equilibrium, 23C | 0.35 | % | ASTM D 570 | |
| Water Absorption, equilibrium, 100°C | 0.58 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method | |
| Melt Flow Rate, 300°C/1.2 kgf | 17.5 | g/10 min | ASTM D 1238 | |
| Density | 1.19 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 16 | cm³/10 min | ISO 1133 | |
| OPTICAL | ||||
| Light Transmission, 2.54 mm | 88 | % | ASTM D 1003 | |
| Haze, 2.54 mm | 1 | % | ASTM D 1003 | |
| Refractive Index | 1.586 | - | ASTM D542 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+17 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in air, 3.2 mm | 14.9 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 50/60 Hz | 3.17 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 2.96 | - | ASTM D 150 | |
| Dissipation Factor, 50/60 Hz | 0.0009 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.01 | - | ASTM D 150 | |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 2.7 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.47 | mm | UL 94 | |
| Oxygen Index (LOI) | 25 | % | ASTM D 2863 | |
| Injection Molding | ||||
| Drying Temperature | 120 | °C | ||
| Drying Time | 3-4 | hrs | ||
| Drying Time (Cumulative) | 48 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 280-305 | °C | ||
| Nozzle Temperature | 275-300 | °C | ||
| Front - Zone 3 Temperature | 280-305 | °C | ||
| Middle - Zone 2 Temperature | 270-295 | °C | ||
| Rear - Zone 1 Temperature | 260-280 | °C | ||
| Mold Temperature | 70-95 | °C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 40-70 | rpm | ||
| Shot to Cylinder Size | 40-60 | % | ||
| Vent Depth | 0.025-0.076 | mm |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺化/物性表參數臺化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用于筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：11374 -
PC/ABS(PC+ABS合金)AC2300/臺化/物性表參數臺化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用于汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：10178 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基于脫模來源于蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：9984 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：8272 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7554 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級，透明高光澤，適用于電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：7401 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：6964 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、復印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：6474 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助于在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表面硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6154 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數科思德塑膠網站提供瑞士EMS化學PA12 TR90的物性表參數下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6020 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：5964 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鐘; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：5919 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對于伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩定性，耐熱性
瀏覽量：5835 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視游樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐沖擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐沖擊性之新材料,一般用于計算機外殼及
瀏覽量：5720 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用于制造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：5623
推薦文章
-
PA66(尼龍66)91G40|Leona(尼胺龍)|旭化成|物性表參數
旭化成Leona(尼胺龍)PA66 91G40是一種表面平滑，低翹曲性。玻璃纖維和礦物填充的尼龍66材料，比重是1.46g/cm3，應用于汽車外部零件。以下是PA66(尼龍66)91G40/Leona(尼胺龍)/旭化成/物性表參數物理性能干燥調節后的單位制測試方法比重1.46--g/cm3ASTM D792,
-
PC/ABS(PC+ABS合金)TN-3411V|TEIJIN(帝人)物性表參數
TEIJIN(帝人)Multilon PC/ABS TN-3411V 是一款 阻燃 級 PC合金材料, 應用于通用 工業與 商務設備 ,Multilon是帝人株式會社開發的PC/ABS 系列的聚合物合金的品牌。 Multilon兼有聚碳酸酯(PC) 樹脂和ABS 樹
-
PP(聚丙烯)HM2300|LUPOL(LG化學)物性表參數
LG化學的Lupol PP HM2300 是一款加30%礦物填料，耐氣候級別的復合聚丙烯,熔融體積流量是8cm/10min,根據物理特性和加工方法其種類也多種多樣,是具有代表性通用塑料中的一種，抗張強度
-
PP(聚丙烯)TB71HW|韓華道達爾(Hanwha)物性表參數
韓華道達爾高抗沖PP TB71HW是超耐氣候性，耐熱復合PP(聚丙烯)作為一種耐氣候性十分優異的復合PP，適合空調室外機零件等室外用途。在PP中放入了無機Filler Talc，剛性和耐熱性大大提高。通過HIPP(High Isotactic Polypropylene)等多種類的 Base PP和韓華道達爾的特殊的加工技術相結合和制成，該產品品質優異。超耐氣候性，耐
-
LCP(工業化液晶聚合物)E525T|寶理塑料|物性表參數
日本寶理LAPEROS LCP E525T 是一種加MD25%增強,SMT對應, 低發塵量的液晶高分子,是我們從傳統的塑料所想象不到的，具有非常特別的結構和性能的高分子，取Themotropic Liquid Crystal Polymer的先頭字
-
PEEK(聚醚醚酮)90G|英國威格斯(VICTREX)物性表參數
英國威格斯VICTREX PEEK 90G 是一種高性能熱塑性材料，無增強聚醚醚酮(PEEK)，半結晶，注射成型用深度過濾顆粒，非常容易流動，符合FDA食品接觸規范，顏色自然/米黃色。 復雜的幾何形狀
-
PC(聚碳酸酯)EXL1182T/沙伯基礎/物性表參數
美國沙伯基礎SABIC LEXAN PC EXL1182T介紹： LEXAN PC EXL1182T 樹脂是聚碳酸酯(PC)硅氧烷共聚物樹脂是一種紫外線穩定、增強的透明注射成型(IM)等級。該樹脂具有良好的低溫(-20 C)延性，與高流量
-
TPE(熱塑性彈性體)TC8FLN/凱柏膠寶/物性表參數
凱柏膠寶KRAIBURG熱塑寶K TPE TC8FLN 是一款自然色, 硬度78A的FR/AP系列TPE材料,用于要求高阻燃性應用的材料解決方案,該化合物無鹵素，擁有自然色和黑色可供選擇，典型應用：開關盒密封件
-
AMILAN(聚酰胺纖維素)CM3511G50|東麗|物性表參數
東麗Nylon樹脂 AMILAN CM3511G50 是一種加50%玻纖增強，高流動級別的尼龍66原料，拉伸強度在23℃測試條件是210MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需求
-
VALOX(沙伯基礎)420/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的 VALOX 420 PBT 是一種加30%GR，具有優異的強度、剛度和尺寸穩定性,高耐熱性,產品電器手柄，聚光燈，電動馬達，連接器。 沙伯基礎創新塑料的VALOX 420 PBT物性表參