VALOX(沙伯基礎)4022/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的VALOX 4022 PBT是一種加20%高強度玻璃纖維增強PBT注塑樹脂，具有良好的機械性能,用途:射燈，電器外殼和把手。
 |
沙伯基礎創新塑料的VALOX 4022 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)4022/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 120 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 120 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 7400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 170 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 170 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5900 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 120 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 120 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7300 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 180 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 175 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 6200 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 130 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 42 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 42 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 560 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 560 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 75 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 75 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 75 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 200 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 3.07E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.32E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 3.04E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.78E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 210 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.45 | - | ASTM D 792 | |
| Filler Content | 20 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.7 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.4-1 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 40 | g/10 min | ASTM D 1238 | |
| Density | 1.45 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.15 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.03 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 16 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 23 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 30 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 140 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.6 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.015 | - | ASTM D 150 | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.6 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.2 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 0.84 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺化/物性表參數臺化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用于筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：11372 -
PC/ABS(PC+ABS合金)AC2300/臺化/物性表參數臺化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用于汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：10176 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基于脫模來源于蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：9980 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：8270 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7554 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)?？寺?Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級，透明高光澤，適用于電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：7401 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：6964 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、復印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：6474 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助于在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表面硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6154 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數科思德塑膠網站提供瑞士EMS化學PA12 TR90的物性表參數下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6019 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：5964 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鐘; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：5919 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對于伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩定性，耐熱性
瀏覽量：5835 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視游樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐沖擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐沖擊性之新材料,一般用于計算機外殼及
瀏覽量：5720 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用于制造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：5623
推薦文章
-
PC合金樹脂/PC-330KZ/鎮江奇美/物性表參數
鎮江奇美WONDERLOY PC合金樹脂PC-330KZ 是一般級，中強度PC合金樹脂,熔融指數是20.g/10min,用途是電子產品外殼，高檔安全帽，鎖螺絲部件，一般成型品,為了增加PC在薄肉產品的耐沖擊性，可
-
PC(聚碳酸酯)3020HF/Samyang(三養)物性表參數
Samyang(三養)TRIREX PC3020HF是一種注塑成型,原料用的聚碳酸酯，比重是1.20g/cm3，熔流率（熔體流動速率）(300°C/1.2 kg)30g/10min，有著優異的機械特性，很好的尺寸穩定性及良好的電氣特性，應用于工業材料,雜貨,電子電器。以下是PC(聚碳酸酯)3020HF/Samyang(三養)物性表參數PROPERTYUNITASTM METHODTYPICAL DATA
-
PA46(尼龍46)TC170|恩驊力(Envalior)物性表參數
恩驊力(Envalior)(原帝斯曼DSM)Stanyl聚合物PA46 TC170 P823C是一款加20%玻纖增強，導熱材料，激光可標記性，注塑成型的PA46原料，應用于LED前照燈照明模塊和透鏡支架，Stanyl作為高性能聚酰胺,在對耐熱性、設計硬度、摩擦磨耗以及流動性都有要求的嚴苛的應用中表現優異，Stanyl能在高達220℃時依舊保持良好的機械性能，這使
-
Bayblend(拜本蘭)T90XG|科思創(PC+ABS合金)物性表參數
科思創Bayblend PC/ABS T90XG 是維卡軟化點溫度/ B 120 = 135C;簡單的流動;金屬化優化表面質量(蒸汽處理). PC/ABS是聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonat
-
PC(聚碳酸酯)3500G30/Samyang(三養)物性表參數
Samyang(三養)TRIREX PC3500G30是一種GF強化,阻燃聚碳酸酯，比重是1.43g/cm3，熔流率（熔體流動速率）(300°C/1.2 kg)7g/10min，有著優異的機械特性，很好的尺寸穩定性及良好的電氣特性，應用于家電,電子電器。以下是PC(聚碳酸酯)3500G30/Samyang(三養)物性表參數PROPERTYUNITASTM METHODTYPICAL DATAPhysicalSpecif
-
PPO(聚苯醚)|NORYL|PX1134/沙伯基礎/物性表參數
沙伯基礎(SABIC)NORYL PPO PX1134 是一種PPE+PS混合(聚苯醚)，這種聚苯醚樹脂是未填充的中耐熱材料，這一等級提供改進的沖擊阻力，以滿足ec儀表板標準，適用于電子/電子市場室內/室外應用
-
PP(聚丙烯)H1500|樂天化學(LOTTE CHEMICAL)物性表參數
樂天化學(LOTTE CHEMICAL)PP H1500是一種注塑級聚丙烯聚合物，比重(23°C)是0.9克/厘米3，熔體流動速率(230°C/2.16kg)是12克/10分鐘，該等級設計用于在常規注塑設備中加工，具有高剛度，熱穩定性，抗劃傷性和高表面光澤度，用于生活用品、食品容器、小型家電產品等。以下是PP(聚丙烯)H1500|樂天化學(LOTTE CHEMICAL)物性表
-
PPS(聚苯硫醚)FZ-6600-R5/日本油墨DIC/物性表參數
日本油墨DIC PPS FZ-6600-R5 是一種玻纖/礦物填充增強的以線性樹脂為基體的PPS復合材料,具有優異的耐水解穩定性,可用于暴露于熱水或汽車冷凍液部件,同時具有優異的熔接強度和一定的韌
-
LCP(工業化液晶聚合物)S140M|日本寶理|物性表參數
日本寶理LAPEROS LCP S140M是一種高耐熱, 高溫剛性,GF40%增強的工業化液晶聚合物,密度1.70g/cm3，拉伸強度120MPa，顏色有：VF2001/BK010P ，阻燃性UL94-V-0,這種材料不但具有不同數量級的機械強度，而且還具有隨著其壁厚的變薄，相對強度反而增加的特異的性能，并且其線性熱膨脹率接近金屬材料。LCP(工業化液晶聚合物)S140
-
塞拉尼斯TPV 191-85PA|Santoprene物性表參數
Celanese(塞拉尼斯)SANTOPRENE(山都坪)TPV 191-85PA是一種熱塑性硫化彈性體，它也是一種柔軟、黑色的特種熱塑性硫化膠(TPV)，它特別適用于與PA-6及其混合物結合，適用于需要硬/軟組合的應用，這種級別的山托丁烯TPV是剪切依賴的，可以在傳統的熱塑性塑料設備上進行注射成型或擠壓加工，它是聚烯烴為基礎的，完全可回收。以下