VALOX(沙伯基礎)4012G/PBT熱塑性聚酯/物性表參數(shù)
沙伯基礎創(chuàng)新塑料SABIC的VALOX 4012G PBT是一種加10%玻璃纖維增強PBT注塑樹脂，具有優(yōu)異的機械性能,應用程序:連接器,該等級為4012，具有更好的循環(huán)時間和延展性。
 |
沙伯基礎創(chuàng)新塑料的VALOX 4012G PBT物性表參數(shù)PDF文檔下載 |
以下是VALOX(沙伯基礎)4012G/PBT熱塑性聚酯/物性表參數(shù)
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 80 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 80 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 4400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3800 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 80 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 80 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4500 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 125 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 120 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 5 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3800 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 110 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 33 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 33 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 380 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 380 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 50 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 4 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 6 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 6 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 205 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 4.63E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 8.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 6.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 4.79E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 2.11E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 205 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 170 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 185 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.35 | - | ASTM D 792 | |
| Filler Content | 10 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.6-1.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.7-1 | % | SABIC method | |
| Melt Flow Rate, 250°C/1.2 kgf | 10 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 90 | g/10 min | ASTM D 1238 | |
| Density | 1.35 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.2 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/1.2 kg | 9 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 50 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 80 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 110 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.4 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.015 | - | ASTM D 150 | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.4 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 | |
| Comparative Tracking Index, M | 150 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 1.6 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 1.5 mm | 800 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 2.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 3.0 mm | 750 | °C | IEC 60695-2-13 | |
| Injection Molding | ||||
| Drying Temperature | 110-120 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250-270 | °C | ||
| Nozzle Temperature | 240-260 | °C | ||
| Front - Zone 3 Temperature | 245-265 | °C | ||
| Middle - Zone 2 Temperature | 240-255 | °C | ||
| Rear - Zone 1 Temperature | 230-245 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 40-100 | °C |
溫馨提示：
本物性表參數(shù)提供者不承擔任何法律責任，建議在選擇材料前，就數(shù)據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯(lián)系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺化/物性表參數(shù)臺化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用于筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數(shù)位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：11373 -
PC/ABS(PC+ABS合金)AC2300/臺化/物性表參數(shù)臺化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用于汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：10178 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基于脫模來源于蔬菜來源。其最突出的特點是優(yōu)良的韌性、水解穩(wěn)定性、耐熱性和耐化
瀏覽量：9984 -
ABS塑料樹脂/PA-757/奇美實業(yè)/物性表參數(shù)奇美實業(yè)POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數(shù)是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：8272 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優(yōu)良的光學性能、良好的可加工性和優(yōu)良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數(shù)PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7554 -
PC(聚碳酸酯)FR6005/科思創(chuàng)(Makrolon)物性表···科思創(chuàng)(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數(shù)MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級，透明高光澤，適用于電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：7401 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：6964 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數(shù)···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、復印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：6474 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規(guī)高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助于在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環(huán)境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表面硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6154 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數(shù)科思德塑膠網站提供瑞士EMS化學PA12 TR90的物性表參數(shù)下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6020 -
Bayblend(拜本蘭)FR3010|科思創(chuàng)(PC/ABS合金···科思創(chuàng)Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：5964 -
Makrolon(模克隆)2407(科思創(chuàng))PC(聚碳酸酯)···科思創(chuàng)Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數(shù)19 厘米 3 /10分鐘; 普通用途; 紫外線穩(wěn)定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：5919 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對于伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩(wěn)定性，耐熱性
瀏覽量：5835 -
PC/ABS(PC+ABS合金)PC-540|奇美實業(yè)|物性表···奇美實業(yè)WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數(shù)是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數(shù)碼產品、變壓器、電視游樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐沖擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐沖擊性之新材料,一般用于計算機外殼及
瀏覽量：5720 -
COC(環(huán)烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優(yōu)異的光學性能，可用于制造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：5623
推薦文章
-
PA6(尼龍6)BM29XH2.0EF/德國朗盛/物性表參數(shù)
德國朗盛 LANXESS Durethan PA6 BM29XH2.0EF 是一種加入30%礦物填充，注塑，改善流動性，熱老化穩(wěn)定尼龍6樹脂，尼龍從環(huán)境中吸收潮氣的能力也不同,這與增塑劑的效果相同，即可以提高材料的
-
LCP(液晶聚酯樹脂)L304M35H|東麗(TORAY)物性表參數(shù)
東麗(TORAY)SIVERAS LCP L304M35H 是一種玻璃纖維＋無機填充物增強,低翹曲, 超良流動，用于電子部件、數(shù)碼家用電器的塑料, SIVERAS由于溶融流動性出色，可以制成更加超薄的成型品。可以低壓
-
ULTEM(沙伯基礎)2110R|PEI(聚醚酰亞胺)物性表參數(shù)
SABIC(沙伯基礎)ULTEM 2110R PEI 樹脂是一種10%的玻璃纖維填充，增強的流動聚醚酰亞胺(tg217c)與內部模具釋放。符合ECO, UL94 V0和5VA listing。 SABIC ULTEM是琥珀色透明固體，不添加任何添加劑就有固有的
-
PC(聚碳酸酯)RX2635/科思創(chuàng)/物性表參數(shù)
德國科思創(chuàng)Makrolon PC RX2635 是全球品級; 體積熔融指數(shù)12厘米3/10分鐘,應用于醫(yī)療設備;適合高能輻射滅菌;生物相容性符合多項ISO 10993-1測試要求;介質粘度;簡單的釋放;醫(yī)療器械透明部件。
-
Makrolon(模克隆)6487|科思創(chuàng)|PC(聚碳酸酯)物性表參數(shù)
科思創(chuàng)Makrolon 6487 PC 是全球品級; 體積熔融指數(shù)MVR (300 C/1.2 kg) 9.0 cm/10 min;加阻燃劑在1.5mm的防火UL94V0抗紫外線PC塑膠原料,介質粘度PC 6487主要用于室外防火產品. Makrolon 6487 PC物性表參數(shù)PD
-
POM(聚甲醛樹脂)NW-02/日本寶理/物性表參數(shù)
日本寶理奪鋼DURACON POM NW-02 是一種滑動性,高韌性的聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放
-
PC(聚碳酸酯)G-3310M|TEIJIN(帝人)物性表參數(shù)
TEIJIN(帝人)Panlite PC G-3310M 是一款添加10%玻璃纖維增強材料的PC塑膠原料，特性是 低異向性 ; 剛性，高 ; 良好的抗蠕變性, 優(yōu)良外觀 , 應用于 工業(yè)與 相機 ，在Japan實現(xiàn)工業(yè)化生產的聚碳酸
-
PP(聚丙烯)AP3AW/埃克森美孚(ExxonMobil)物性表參數(shù)
埃克森美孚(ExxonMobil)PP AP3AW是一種具有紫外線穩(wěn)定性、中等抗沖擊強度的共聚物樹脂，熔體流動速率(230°C/2.16kg)是10克/10分鐘，密度(23°C)是0.9克/厘米3，用于汽車蓄電池箱。以下是PP(聚丙烯)AP3AW/埃克森美孚(ExxonMobil)物性表參數(shù)基本信息黃卡編號E225564-550934特性低翹曲性剛性，高抗紫外線性能良好流動性中等
-
POM(聚甲醛樹脂)4513|旭化成(AsahiKASEI)物性表參數(shù)
旭化成(AsahiKASEI)Tenac-C(鐵耐克-C)POM 4513是標準流動等級，耐候性等級，含有紫外線吸收劑和其他添加劑，因而具有良好的耐候性的聚甲醛樹脂，密度 1.41(g/cm3)，彎曲模量2450 (MPa) ，簡支梁缺口沖擊強度7.0(kJ/m2) ，典型用途領域包括工程/工業(yè)配件、房屋和汽車行業(yè)。Tenac-C(鐵耐克-C) POM 4513物性表參數(shù)PDF文檔下載
-
PP(聚丙烯聚合物)SFC-650BT/樂天化學/物性表參數(shù)
樂天化學(LOTTE CHEMICAL)PP SFC-650BT是一種聚丙烯聚合物，比重(23°C)是0.9克/厘米3，熔體流動速率(230°C/2.16kg)是8克/10分鐘，該等級可控介質改性丙烯無規(guī)共聚物，用于制造高透明鑄膜，本產品含有防滑劑和防堵劑，它具有良好的加工性，優(yōu)異的清晰度和光澤，該樹脂是專門設計的，不會褪色，并提供優(yōu)異的薄膜光學性能