PC(聚碳酸酯)XHT4143T/沙伯基礎(SABIC)物性表參數

日期：2020-06-22 02:44:00 編輯：科思德塑膠來源：科思德塑膠瀏覽：407

沙伯基礎創新塑料（SABIC）LEXAN PC XHT4143T是一種高流動、抗紫外線，高耐熱的聚碳酸酯共聚物，溶化體積流率（MVR)(330°C/2.16 kg)24.0cm³/10min，耐高溫高達162度，它有一系列透明顏色。

PC(聚碳酸酯)XHT4143T/沙伯基礎(SABIC)物性表參數PDF文檔下載

以下是PC(聚碳酸酯)XHT4143T/沙伯基礎(SABIC)物性表參數

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	77	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	69	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	7	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	50	%	ASTM D 638
Tensile Modulus, 5 mm/min	2730	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	120	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2600	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	78	MPa	ISO 527
Tensile Stress, break, 50 mm/min	67	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	7	%	ISO 527
Tensile Strain, break, 50 mm/min	50	%	ISO 527
Tensile Modulus, 1 mm/min	2750	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	80	MPa	ISO 178
Flexural Modulus, 2 mm/min	2600	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C	93	J/m	ASTM D 256
Izod Impact, notched, -30°C	76	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	72	J	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80103 +23°C	10	kJ/m²	ISO 180/1A
Izod Impact, notched 80103 -30°C	8	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	11	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	9	kJ/m²	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m²	ISO 179/1eU
THERMAL
Vicat Softening Temp, Rate B/50	183	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	174	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	165	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	6.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	6.E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 165°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	183	°C	ISO 306
Vicat Softening Temp, Rate B/120	181	°C	ISO 306
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	173	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	162	°C	ISO 75/Af
PHYSICAL
Specific Gravity	1.2	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.6-0.95	%	SABIC method
Melt Flow Rate, 330°C/2.16 kgf	25	g/10 min	ASTM D 1238
Density	1.21	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.33	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.25	%	ISO 62
Melt Volume Rate, MVR at 330°C/2.16kg	24	cm³/10 min	ISO 1133
OPTICAL
Light Transmission, 2.54 mm	86	%	ASTM D 1003
Haze, 2.54 mm	-0.5	%	ASTM D 1003
Refractive Index	1.605	-	ASTM D542
FLAME CHARACTERISTICS
Glow Wire Flammability Index 850°C, passes at	2	mm	IEC 60695-2-12
Glow Wire Flammability Index 960°C, passes at	2.5	mm	IEC 60695-2-12
Injection Molding
Drying Temperature	135	°C
Drying Time	4-6	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	290-325	°C
Nozzle Temperature	295-310	°C
Front - Zone 3 Temperature	300-315	°C
Middle - Zone 2 Temperature	290-305	°C
Rear - Zone 1 Temperature	280-295	°C
Mold Temperature	95-130	°C
Back Pressure	0.3-0.7	MPa
Screw Speed	40-90	rpm
Shot to Cylinder Size	40-60	%
Vent Depth	0.025-0.08	mm