PC(聚碳酸酯)EXL9134/沙伯基礎(SABIC)物性表參數

日期：2020-06-16 02:22:48 編輯：科思德塑膠來源：科思德塑膠瀏覽：1436

SABIC(沙伯基礎創新塑料)LEXAN PC EXL9134是不透明PC加硅氧烷共聚物，也是一種UV穩定高流動不透明注塑(IM)級樹脂，該樹脂提供UL94 V0 @ 1.5mm的阻燃性能，基于非溴、非氯FR系統，低溫延展性(-40℃)的特性和優異的加工性能，與標準PC相比，IM周期更短，LEXAN EXL9134樹脂是一種產品可在廣泛的不透明顏色。

PC(聚碳酸酯)EXL9134/沙伯基礎(SABIC)物性表參數PDF文檔下載

以下是PC(聚碳酸酯)EXL9134/沙伯基礎(SABIC)物性表參數

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E45329-591113	-	-
UL Yellow Card Link 2		E45329-591114	-	-
UL Recognized, 94-5VA Flame Class Rating		≥3	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating		≥1.5	mm	UL 94
Glow Wire Ignitability Temperature, 3.0 mm		825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm		825	°C	IEC 60695-2-13
Glow Wire Flammability Index, 3.0 mm		960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.5 mm		960	°C	IEC 60695-2-12
UV-light, water exposure/immersion		F1	-	UL 746C
Glow Wire Flammability Index 960°C, passes at		≥1.5	mm	IEC 60695-2-12
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min		58	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min		59	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min		6	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min		115	%	ASTM D 638
Tensile Modulus, 5 mm/min		2100	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span		92	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span		2400	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min		56	MPa	ISO 527
Tensile Stress, break, 50 mm/min		57	MPa	ISO 527
Tensile Strain, yield, 50 mm/min		6	%	ISO 527
Tensile Strain, break, 50 mm/min		108	%	ISO 527
Tensile Modulus, 1 mm/min		2000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min		87	MPa	ISO 178
Flexural Modulus, 2 mm/min		2100	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C		785	J/m	ASTM D 256
Izod Impact, notched, -30°C		655	J/m	ASTM D 256
Izod Impact, notched, -40°C		380	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C		67	J	ASTM D 3763
Izod Impact, unnotched 80103 +23°C		NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80103 -30°C		NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80103 +23°C		65	kJ/m²	ISO 180/1A
Izod Impact, notched 80103 -30°C		30	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm		70	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm		35	kJ/m²	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm		NB	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm		NB	kJ/m²	ISO 179/1eU
THERMAL
Vicat Softening Temp, Rate B/50		140	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed		123	°C	ASTM D 648
CTE, -40°C to 40°C, flow		6.1E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow		6.2E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow		6.1E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow		6.2E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50		139	°C	ISO 306
Vicat Softening Temp, Rate B/120		141	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm		118	°C	ISO 75/Af
Relative Temp Index, Elec	¹⁾	125	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	115	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	125	°C	UL 746B
PHYSICAL
Specific Gravity		1.19	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm		0.4-0.8	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf		16	g/10 min	ASTM D 1238
Density		1.19	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)		0.4	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)		0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg		15	cm³/10 min	ISO 1133
ELECTRICAL
Comparative Tracking Index (UL) {PLC}		3	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 2		≥3	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 3		≥0.7	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 0		≥3	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 1		≥0.7	mm	UL 746A
Injection Molding
Drying Temperature		120	°C
Drying Time		3-4	hrs
Drying Time (Cumulative)		48	hrs
Maximum Moisture Content		0.02	%
Melt Temperature		295-315	°C
Nozzle Temperature		290-310	°C
Front - Zone 3 Temperature		295-315	°C
Middle - Zone 2 Temperature		280-305	°C
Rear - Zone 1 Temperature		270-295	°C
Mold Temperature		70-95	°C
Back Pressure		0.3-0.7	MPa
Screw Speed		40-70	rpm
Shot to Cylinder Size		40-60	%
Vent Depth		0.025-0.076	mm