PC(聚碳酸酯)EXL4019/沙伯基礎(SABIC)物性表參數

日期：2020-06-12 06:30:29 編輯：科思德塑膠來源：科思德塑膠瀏覽：474

SABIC(沙伯基礎創新塑料)LEXAN PC EXL4019是不透明的加9%玻璃纖維(GF)增強聚碳酸酯(PC)硅氧烷共聚物樹脂，用于需要提高剛度的注射成型(IM)應用，與常規的GF增強PC樹脂相比，這種樹脂還具有更好的延性，具有介質流動特性和優異的加工性能，與標準PC相比，IM周期更短，LEXAN EXL4019樹脂是一個很好的廣泛的應用，只有有限的顏色可供選擇。

PC(聚碳酸酯)EXL4019/沙伯基礎(SABIC)物性表參數PDF文檔下載

以下是PC(聚碳酸酯)EXL4019/沙伯基礎(SABIC)物性表參數

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 5 mm/min	55	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	45	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	4.3	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	14	%	ASTM D 638
Tensile Modulus, 5 mm/min	3950	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	103	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	3500	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	54	MPa	ISO 527
Tensile Stress, break, 5 mm/min	48	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4.3	%	ISO 527
Tensile Strain, break, 5 mm/min	8.7	%	ISO 527
Tensile Modulus, 1 mm/min	3900	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	98	MPa	ISO 178
Flexural Modulus, 2 mm/min	3450	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C	345	J/m	ASTM D 256
Izod Impact, notched, -30°C	150	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	40	J	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80103 +23°C	25	kJ/m²	ISO 180/1A
Izod Impact, notched 80103 -30°C	10	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	25	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	15	kJ/m²	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m²	ISO 179/1eU
THERMAL
Vicat Softening Temp, Rate B/50	146	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	137	°C	ASTM D 648
CTE, -40°C to 40°C, flow	4.7E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	4.7E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C	Passes	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	146	°C	ISO 306
Vicat Softening Temp, Rate B/120	146	°C	ISO 306
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	135	°C	ISO 75/Ae
PHYSICAL
Specific Gravity	1.25	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.2-0.6	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.2-0.6	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf	7.5	g/10 min	ASTM D 1238
Density	1.25	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.15	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.4	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	6	cm³/10 min	ISO 1133
Injection Molding
Drying Temperature	120	°C
Drying Time	3-4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	310-330	°C
Nozzle Temperature	305-325	°C
Front - Zone 3 Temperature	310-330	°C
Middle - Zone 2 Temperature	300-320	°C
Rear - Zone 1 Temperature	290-310	°C
Mold Temperature	80-115	°C
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	40-60	%
Vent Depth	0.025-0.076	mm