PC/PC1004R/PC物性表參數

日期：2020-04-20 03:52:23 編輯：科思德塑膠來源：科思德塑膠瀏覽：805

沙伯基礎SABIC塑料PC PC1004R是一種中低流動（MFR = 10,300°C / 1.2kg），天然，FDA食品接觸投訴，熱穩定，聚碳酸酯產品，脫模劑設計用于通用成型市場。

以下是沙伯基礎SABIC塑料PC PC1004R物性表參數

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	¹⁾	63	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min		6	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min		>70	%	ASTM D 638
Tensile Modulus, 50 mm/min		2350	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span		90	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span		2300	MPa	ASTM D 790
Hardness, Rockwell R		120	-	ASTM D 785
Tensile Stress, yield, 50 mm/min		63	MPa	ISO 527
Tensile Strain, yield, 50 mm/min		6	%	ISO 527
Tensile Strain, break, 50 mm/min		>70	%	ISO 527
Tensile Modulus, 1 mm/min		2350	MPa	ISO 527
Flexural Stress, yield, 2 mm/min		90	MPa	ISO 178
Flexural Modulus, 2 mm/min		2300	MPa	ISO 178
Hardness, Rockwell R		120	-	ISO 2039-2
IMPACT
Izod Impact, unnotched, 23°C		NB	J/m	ASTM D 4812
Izod Impact, notched, 23°C		800	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C		65	J	ASTM D 3763
Izod Impact, unnotched 80103 +23°C		NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80103 -30°C		NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80103 +23°C		70	kJ/m²	ISO 180/1A
Izod Impact, notched 80103 -30°C		12	kJ/m²	ISO 180/1A
THERMAL
Vicat Softening Temp, Rate B/50		143	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm		138	°C	ASTM D 648
HDT, 1.82 MPa, 3.2 mm		127	°C	ASTM D 648
CTE, -40°C to 95°C, flow		7.E-05	1/°C	ASTM E 831
Thermal Conductivity		0.2	W/m-°C	ASTM C177
Thermal Conductivity		0.2	W/m-°C	ISO 8302
CTE, 23°C to 80°C, flow		7.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C		Passes	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50		143	°C	ISO 306
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm		138	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm		127	°C	ISO 75/Af
PHYSICAL
Specific Gravity		1.2	-	ASTM D 792
Water Absorption, equilibrium, 23C		0.35	%	ASTM D 570
Mold Shrinkage on Tensile Bar, flow		0.5-0.7	%	SABIC method
Mold Shrinkage, flow, 3.2 mm	²⁾	0.5-0.7	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf		10	g/10 min	ASTM D 1238
Density		1.2	g/cm³	ISO 1183
Water Absorption, (23°C/sat)		0.35	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg		9	cm³/10 min	ISO 1133
OPTICAL
Light Transmission, 2.54 mm		88-90	%	ASTM D 1003
Haze, 2.54 mm		<0.8	%	ASTM D 1003
Refractive Index		1.586	-	ASTM D542
Refractive Index		1.586	-	ISO 489
ELECTRICAL
Volume Resistivity		>1.E+15	Ohm-cm	ASTM D 257
Dielectric Strength, 1.6 mm		27	kV/mm	ASTM D 149
Relative Permittivity, 60 Hz		3	-	ASTM D 150
Relative Permittivity, 1 MHz		3	-	ASTM D 150
Dissipation Factor, 60 Hz		0.001	-	ASTM D 150
Dissipation Factor, 1 MHz		0.01	-	ASTM D 150
Volume Resistivity		>1.E+15	Ohm-cm	IEC 60093
Dielectric Strength, 1.6 mm		27	kV/mm	IEC 60243-1
Relative Permittivity, 60 Hz		3	-	IEC 60250
Relative Permittivity, 1 MHz		3	-	IEC 60250
Dissipation Factor, 60 Hz		0.001	-	IEC 60250
Dissipation Factor, 1 MHz		0.01	-	IEC 60250
FLAME CHARACTERISTICS
UL Recognized, 94V-2 Flame Class Rating	³⁾	1.6	mm	UL 94
Injection Molding
Drying Temperature		120	°C
Drying Time		2-4	hrs
Maximum Moisture Content		0.02	%
Melt Temperature		280-310	°C
Nozzle Temperature		270-290	°C
Front - Zone 3 Temperature		280-310	°C
Middle - Zone 2 Temperature		270-290	°C
Rear - Zone 1 Temperature		260-280	°C
Hopper Temperature		60-80	°C
Mold Temperature		80-110	°C

1）僅限典型值。對于各種顏色，正常公差范圍內的變化是可能的。在23℃/ 50％相對濕度下儲存至少48小時后測量所有值。除熔體體積和熔體流動速率外，所有性能均在注塑樣品上測量。根據ISO 294制備在ISO測試標準下測試的所有樣品。
2）由實驗室試樣制成的測量值。由于加工條件，設備，零件幾何形狀和工具設計的不同，實際收縮率可能會超出范圍。建議在切割新模塑制品的工具之前，使用替代或傳統工具進行模具收縮研究。

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.

上一頁：PC(聚碳酸酯)PC1003R|SABIC(沙伯基礎)物性表參數下一頁：PC(聚碳酸酯)PC1500|SABIC(沙伯基礎)物性表參數

返回首頁返回物性參數列表