LEXAN(沙伯基礎)FL905/PC(聚碳酸酯)物性表參數

日期：2020-04-20 03:20:25 編輯：科思德塑膠來源：科思德塑膠瀏覽：374

沙伯基礎SABIC塑料LEXAN FL905聚碳酸酯（PC）是一種可注塑成型的非氯化/溴化，5％玻璃填充，可發泡的阻燃級，具有良好的抗沖擊性能，它的MVR為3（300°C / 1.2kg），UL94 V0 @ 3mm，5VA @ 6.0mm。

沙伯基礎SABIC塑料LEXAN FL905 PC物性表參數PDF文檔下載

以下是LEXAN(沙伯基礎)FL905/PC(聚碳酸酯)物性表參數

ROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	58	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	47	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	5.7	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	30	%	ASTM D 638
Tensile Modulus, 50 mm/min	2810	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	98	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2670	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	57	MPa	ISO 527
Tensile Stress, break, 50 mm/min	44	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5.9	%	ISO 527
Tensile Strain, break, 50 mm/min	25	%	ISO 527
Tensile Modulus, 1 mm/min	2790	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	91	MPa	ISO 178
Flexural Modulus, 2 mm/min	2680	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C	520	J/m	ASTM D 256
Izod Impact, notched, -30°C	137	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	53	J	ASTM D 3763
Instrumented Impact Total Energy, -30°C	46	J	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	171	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	172	kJ/m²	ISO 180/1U
Izod Impact, notched 80103 +23°C	27	kJ/m²	ISO 180/1A
Izod Impact, notched 80103 -30°C	12	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	31	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	16	kJ/m²	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	335	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	313	kJ/m²	ISO 179/1eU
THERMAL
Vicat Softening Temp, Rate A/50	148	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	146	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	140	°C	ASTM D 648
CTE, -40°C to 95°C, flow	5.4E-05	1/°C	ASTM E 831
CTE, -40°C to 95°C, xflow	8E-05	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	5.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.6E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	147	°C	ISO 306
Vicat Softening Temp, Rate B/120	149	°C	ISO 306
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	145	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	134	°C	ISO 75/Af
PHYSICAL
Specific Gravity	1.2	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.6	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.5	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf	3.2	g/10 min	ASTM D 1238
Density	1.2	g/cm³	ISO 1183
Melt Volume Rate, MVR at 300°C/1.2 kg	3	cm³/10 min	ISO 1133
FLAME CHARACTERISTICS
FOAM - Flame Class Minimum Density	0.9	g/cm³	-
UL Recognized, 94V-0 Flame Class Rating	3	mm	UL 94
UL Recognized, 94-5VA Flame Class Rating	6	mm	UL 94
Injection Molding
Drying Temperature	120	°C
Drying Time	3-4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	.02	%
Melt Temperature	295-315	°C
Nozzle Temperature	290-310	°C
Front - Zone 3 Temperature	295-315	°C
Middle - Zone 2 Temperature	280-305	°C
Rear - Zone 1 Temperature	270-295	°C
Mold Temperature	70-95	°C
Back Pressure	.3-.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	40-60	%
Vent Depth	.02-.076	mm