VALOX(沙伯基礎)VX5022/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的VALOX VX5022 PBT是一種加20%玻璃纖維增強PBT+PC共混物，具有低翹曲性能,這個等級是5021，減少翹曲。
 |
沙伯基礎創新塑料的VALOX VX5022 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)VX5022/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 7300 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 145 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5800 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7100 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 6300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 205 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 50 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 645 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 65 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 200 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 2.49E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.87E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.43E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 200 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.39 | - | ASTM D 792 | |
| Filler Content | 20 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.5 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.9 | % | SABIC method | |
| Melt Flow Rate, 250°C/2.16 kgf | 16 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Density | 1.39 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 13 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 28 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 215 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.3 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.014 | - | ASTM D 150 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+16 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+16 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 100 Hz | 3.3 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 100 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Comparative Tracking Index, M | 100 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Flammability Index 850°C, passes at | 2 | mm | IEC 60695-2-12 | |
| Oxygen Index (LOI) | 23 | % | ISO 4589 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺化/物性表參數臺化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用于筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：11373 -
PC/ABS(PC+ABS合金)AC2300/臺化/物性表參數臺化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用于汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：10178 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基于脫模來源于蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：9984 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：8272 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7554 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級，透明高光澤，適用于電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：7401 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：6964 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、復印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：6474 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助于在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表面硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6154 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數科思德塑膠網站提供瑞士EMS化學PA12 TR90的物性表參數下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6020 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：5964 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鐘; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：5919 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對于伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩定性，耐熱性
瀏覽量：5835 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視游樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐沖擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐沖擊性之新材料,一般用于計算機外殼及
瀏覽量：5720 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用于制造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：5623
推薦文章
-
POM(聚甲醛樹脂)YF-5/日本寶理/物性表參數
日本寶理奪鋼DURACON POM YF-5 是加5%鐵氟龍PTFE,滑動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放
-
XYRON(采龍)X552V|旭化成|PPO(聚苯醚)物性表參數
旭化成XYRON PPO X552V 是一種加入20%填料,低翹曲性, 外觀良好的阻燃級PPE/PS原料，特點: 良好的耐熱性、尺寸穩定性和機械性能，應用領域: 汽車零件，電氣和電子零件，工業零件，高
-
PC（聚碳酸酯）XHT4141|沙伯基礎|物性表參數
沙伯基礎PC XHT4141是一種高流動、高耐熱聚碳酸酯共聚物，它有一系列不透明和透明的顏色可供選擇。以下是PC（聚碳酸酯）XHT4141|沙伯基礎|物性表參數物理性能額定值單位制測試方法比重 --1.20g/cm3ASTM D792--1.21g/cm3ISO 1183熔流率（熔體流動速率） (330°C/2.16 kg)
-
TOYOLAC(東麗)100G-30|ABS塑料樹脂|物性表參數
東麗TOYOLAC ABS 100G-30 是一種加30%玻纖，簡支梁沖擊強度是7/kJ/m 2 ，玻璃纖維增強級別的ABS樹脂，廣泛用在工業和家庭用品中，這是因為其具有一系列獨特的性質（兼具強度、輕便性
-
PBT(聚對苯二甲酸丁二酯)701SA|寶理塑料|物性表參數
日本寶理DURANEX PBT 701SA 是一種GF增強, 低比重, 低磨耗型,低翹曲,SA系列的聚酯聚合物,由于它具有高的熔點和結晶度，由于其吸水率和線性熱膨脹系數很低，因此具有優良的尺寸穩定性。
-
PP(聚丙烯)SJ-170T|樂天化學(LOTTE CHEMICAL)物性表參數
樂天化學(LOTTE CHEMICAL)PP SJ-170T是一種注塑級聚丙烯聚合物，比重(23°C)是0.9克/厘米3，熔體流動速率(230°C/2.16kg)是17克/10分鐘，這種等級的設計是在傳統的注射成型設備中加工，SJ-170T具有良好的熱穩定性和高熔體流動性，它通常用于生產家庭用品，透明文具。以下是PP(聚丙烯)SJ-170T|樂天化學(LOTTE CHEMICAL)物
-
PC(聚碳酸酯)4795R/沙伯基礎(SABIC)物性表參數
SABIC(沙伯基礎創新塑料)LEXAN PC 4795R 是一種高熱聚碳酸酯共聚物，具有良好的阻燃性、加工性和沖擊強度的平衡,可有一系列透明的顏色。 PC(聚碳酸酯)4795R/沙伯基礎(SABIC)物性表參數PDF文
-
TPV(熱塑性硫化橡膠)101-87/塞拉尼斯/物性表參數
塞拉尼斯Santoprene TPV 101-87是一種硬度94A黑色的TPV(熱塑性硫化彈性體)，這種材料同時具有良好的物理性質和耐化學性，適用于廣泛的領域，這一牌 號的TPV 是剪切速率依賴型產品，可在常規熱塑性注塑成型或擠出成型設 備上加工，這是一種聚烯烴基材料，可在生產過程中進行回收利用。TPV(熱塑性硫化橡膠)101-87/塞拉尼斯/物
-
ABS塑料樹脂/PA-757/奇美實業/物性表參數
奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
-
PC(聚碳酸酯)M3020PN/Samyang(三養)物性表參數
Samyang(三養)TRIREX PCM3020PN是一種非強化,阻燃 (V0, 5VA)，光擴散聚碳酸酯，比重是1.18g/cm3，熔流率（熔體流動速率）(300°C/1.2 kg)30g/10min，有著優異的機械特性，很好的尺寸穩定性及良好的電氣特性，應用于OA,家電。以下是PC(聚碳酸酯)M3020PN/Samyang(三養)物性表參數PROPERTYUNITASTM METHODTYPICAL DATAP