VALOX(沙伯基礎)V3004/PBT熱塑性聚酯/物性表參數(shù)

日期：2020-04-20 02:00:15 編輯：科思德塑膠來源：科思德塑膠瀏覽：317

沙伯基礎創(chuàng)新塑料SABIC的VALOX V3004 PBT是一種用彈性體改性的未填充PBT,適用于柔性鉸鏈、汽車連接器、薄膜應用。

沙伯基礎創(chuàng)新塑料的VALOX V3004 PBT物性表參數(shù)PDF文檔下載

以下是VALOX(沙伯基礎)V3004/PBT熱塑性聚酯/物性表參數(shù)

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	51	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	22	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	4	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	300	%	ASTM D 638
Tensile Modulus, 50 mm/min	2400	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	82	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2300	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	50	MPa	ISO 527
Tensile Stress, break, 50 mm/min	30	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3.7	%	ISO 527
Tensile Strain, break, 50 mm/min	200	%	ISO 527
Tensile Modulus, 1 mm/min	2350	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	74	MPa	ISO 178
Flexural Modulus, 2 mm/min	2100	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C	51	J/m	ASTM D 256
Izod Impact, notched, -30°C	45	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	60	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	4	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	7	kJ/m²	ISO 179/1eA
THERMAL
Vicat Softening Temp, Rate B/50	167	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	120	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	52	°C	ASTM D 648
CTE, -40°C to 40°C, flow	9.18E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.5E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	9.18E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.5E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	165	°C	ISO 306
Vicat Softening Temp, Rate B/120	170	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	48	°C	ISO 75/Af
PHYSICAL
Specific Gravity	1.29	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	2.1-2.7	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	2.1-2.7	%	SABIC method
Melt Flow Rate, 250°C/2.16 kgf	23	g/10 min	ASTM D 1238
Density	1.29	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.2	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.08	%	ISO 62
Melt Volume Rate, MVR at 250°C/2.16 kg	21	cm³/10 min	ISO 1133
Injection Molding
Drying Temperature	120	°C
Drying Time	3-4	hrs
Drying Time (Cumulative)	12	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250-265	°C
Nozzle Temperature	245-260	°C
Front - Zone 3 Temperature	250-265	°C
Middle - Zone 2 Temperature	245-260	°C
Rear - Zone 1 Temperature	240-255	°C
Mold Temperature	50-75	°C
Back Pressure	0.3-0.7	MPa
Screw Speed	50-100	rpm
Shot to Cylinder Size	40-80	%
Vent Depth	0.025-0.038	mm