VALOX(沙伯基礎(chǔ))745/PBT熱塑性聚酯/物性表參數(shù)

日期：2020-04-18 04:27:49 編輯：科思德塑膠來(lái)源：科思德塑膠瀏覽：299

沙伯基礎(chǔ)創(chuàng)新塑料SABIC的VALOX 745 PBT是一種加30%礦物增強(qiáng)聚酯改善韌性和低翹曲,典型的應(yīng)用是電話鈴聲框架和卡片架。

沙伯基礎(chǔ)創(chuàng)新塑料的VALOX 745 PBT物性表參數(shù)PDF文檔下載

以下是VALOX(沙伯基礎(chǔ))745/PBT熱塑性聚酯/物性表參數(shù)

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	48	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	46	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	89	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	3440	MPa	ASTM D 790
Hardness, Rockwell R	112	-	ASTM D 785
IMPACT
Izod Impact, unnotched, 23°C	1602	J/m	ASTM D 4812
Izod Impact, notched, 23°C	80	J/m	ASTM D 256
THERMAL
HDT, 0.45 MPa, 6.4 mm, unannealed	160	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	87	°C	ASTM D 648
CTE, -40°C to 40°C, flow	7.56E-05	1/°C	ASTM E 831
CTE, 60°C to 138°C, flow	1.39E-04	1/°C	ASTM E 831
Relative Temp Index, Elec	105	°C	UL 746B
Relative Temp Index, Mech w/impact	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	105	°C	UL 746B
PHYSICAL
Specific Gravity	1.46	-	ASTM D 792
Specific Volume	0.69	cm³/g	ASTM D 792
Water Absorption, 24 hours	0.09	%	ASTM D 570
Mold Shrinkage, flow, 3.2 mm	0.8-1	%	SABIC method
Mold Shrinkage, flow, 1.5-3.2 mm	0.6-0.8	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.8-1	%	SABIC method
Mold Shrinkage, xflow, 1.5-3.2 mm	0.6-0.8	%	SABIC method
ELECTRICAL
Volume Resistivity	6.9E+16	Ohm-cm	ASTM D 257
Dielectric Strength, in air, 3.2 mm	23.2	kV/mm	ASTM D 149
Dielectric Strength, in oil, 1.6 mm	24.8	kV/mm	ASTM D 149
Relative Permittivity, 100 Hz	3.3	-	ASTM D 150
Relative Permittivity, 1 MHz	3.2	-	ASTM D 150
Dissipation Factor, 100 Hz	0.002	-	ASTM D 150
Dissipation Factor, 1 MHz	0.014	-	ASTM D 150
Arc Resistance, Tungsten {PLC}	5	PLC Code	ASTM D 495
Hot Wire Ignition {PLC)	2	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	3	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	0	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	2	PLC Code	UL 746A
FLAME CHARACTERISTICS
UL Recognized, 94HB Flame Class Rating	1.47	mm	UL 94
Injection Molding
Drying Temperature	120	°C
Drying Time	3-4	hrs
Drying Time (Cumulative)	12	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	255-275	°C
Nozzle Temperature	255-270	°C
Front - Zone 3 Temperature	255-265	°C
Middle - Zone 2 Temperature	250-260	°C
Rear - Zone 1 Temperature	245-255	°C
Mold Temperature	65-95	°C
Back Pressure	0.3-0.7	MPa
Screw Speed	50-80	rpm
Shot to Cylinder Size	40-80	%
Vent Depth	0.025-0.038	mm