PA6(尼龍6)B30S/德國朗盛/物性表參數

日期：2020-04-25 02:39:45 編輯：科思德塑膠來源：科思德塑膠瀏覽：1364

德國朗盛Durethan PA6 B30S是一種無強化，壓縮成型，加工過程中減少排放，不易變形尼龍樹脂,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一系列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。

PA6 B30S物性表參數PDF文檔下載

生產商：LANXESS(德國朗盛)、品名：Durethan
PA6(尼龍6)B30S/德國朗盛/物性表參數

C	These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 270 °C / WZ 80 °C; 500 bar	%	acc. ISO 2577	1.02
	Molding shrinkage, transverse	150x105x3; 270 °C / WZ 80 °C; 500 bar	%	acc. ISO 2577	1.16
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.32
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.4
Mechanical properties (23 °C/50 % r. h.)
C	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	3200	1000
C	Yield stress	50 mm/min	MPa	ISO 527-1,-2	80	40
C	Yield strain	50 mm/min	%	ISO 527-1,-2	4.0	20
C	Nominal strain at break	50 mm/min	%	ISO 527-1,-2	20	> 50
C	Tensile creep modulus	1 h	MPa	ISO 899-1		800
C	Tensile creep modulus	1000 h	MPa	ISO 899-1		600
C	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	N	N
C	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	N	N
C	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	< 10	20
C	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	N	N
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	N	N
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	< 10	30
	Flexural modulus	2 mm/min	MPa	ISO 178-A	2900	850
	Flexural strength	2 mm/min	MPa	ISO 178-A	110	35
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	6.0	8.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	95	25
C	Puncture maximum force	23 °C	N	ISO 6603-2	5900
C	Puncture maximum force	-30 °C	N	ISO 6603-2	7300
C	Puncture energy	23 °C	J	ISO 6603-2	90
C	Puncture energy	-30 °C	J	ISO 6603-2	85
	Ball indentation hardness		N/mm²	ISO 2039-1	140	50
Thermal properties
C	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
C	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	55
C	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	160
C	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	45
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	200
C	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	1.0
C	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	1.1
C	Burning behavior UL 94	1.5 mm	Class	UL 94	V-2
C	Burning behavior UL 94	0.4 mm	Class	UL 94	V-2
C	Oxygen index	Method A	%	ISO 4589-2	26
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	750
	Burning behavior US-FMVSS302	>=1.0 mm		ISO 3795	passed
C	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	200
Electrical properties (23 °C/50 % r. h.)
C	Relative permittivity	100 Hz	-	IEC 60250	4.0	15
C	Relative permittivity	1 MHz	-	IEC 60250	3.5	4.0
C	Dissipation factor	100 Hz	10-4	IEC 60250	170	2000
C	Dissipation factor	1 MHz	10-4	IEC 60250	200	1200
C	Volume resistivity		Ohm·m	IEC 60093	1E13	1E10
C	Surface resistivity		Ohm	IEC 60093	1E14	1E13
C	Electric strength	1 mm	kV/mm	IEC 60243-1	30	30
C	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
	Comparative tracking index CTI M	Solution B	Rating	IEC 60112	600 M
Other properties (23 °C)
C	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	10
C	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	3
C	Density		kg/m³	ISO 1183	1140
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
C	Injection molding-Melt temperature		°C	ISO 294	270
C	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	260-280
	Mold temperature		°C	-	80-100