PA66(尼龍66)AKV50/德國朗盛/物性表參數

日期：2020-04-25 02:37:53 編輯：科思德塑膠來源：科思德塑膠瀏覽：432

德國朗盛Durethan PA66 AKV50是一種加50%玻璃纖維p66, 注塑成型，熱老化穩定，表面光潔度提高尼龍樹脂,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一系列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
生產商：LANXESS(德國朗盛)、品名：Durethan
PA66(尼龍66)AKV50/德國朗盛/物性表參數

C	These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 300 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.23
	Molding shrinkage, transverse	150x105x3; 300 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	1.25
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.02
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.03
Mechanical properties (23 °C/50 % r. h.)
C	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	15700	10700
C	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	220	170
C	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.5	4.0
C	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	95	95
C	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	100	100
C	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	19	23
C	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	15	15
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	14	18
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	11	11
	Flexural modulus	2 mm/min	MPa	ISO 178-A	14000	10300
	Flexural strength	2 mm/min	MPa	ISO 178-A	370	250
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.0	5.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A		235
	Ball indentation hardness		N/mm²	ISO 2039-1	290	160
Thermal properties
C	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	263
C	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	~250
C	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	~250
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 230
Other properties (23 °C)
C	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	~4
C	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	~1.4
C	Density		kg/m³	ISO 1183	1570
	Bulk density		kg/m³	ISO 60	~700
Processing conditions for test specimens
C	Injection molding-Melt temperature		°C	ISO 294	300
C	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120

德國朗盛Durethan PA66 AKV50具有高抗震及抗裂性能，具體指標與材料的等級與含水量有關。彈性體改性的材料即使在低含水量及低溫下也具有良好的韌性,硬度高，尤其對于玻纖增強級別產品；拉伸模量：1,300 到 15,700 MPa (取決于含水量),良好的機械性能及阻尼吸聲效應、低摩擦力、急速運行能力好，氣體阻隔性能好（薄膜級）.

密度	1.01~1.23	模具溫度	80.0 到 100°C
加工（熔體）溫度	260 到 270°C	注射壓力	230 到 250°C
預熱	溫度/°C	130°C	工藝參數	注射時間	20~90
時間/h	4.0hr	高壓時間	0~5
料桶溫度/°C	后段	193 到 238°C	冷卻時間	20~90
中段	210 到 249°C	總周期	220 到 260°C
前段	221 到 254°C	螺桿轉數	30 到 60rpm
噴嘴溫度	232 到 274°C	使用注射機類型	螺桿式

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.

上一頁：PA66(尼龍66)AKV40H3.0/德國朗盛/物性表參數下一頁：PA66(尼龍66)AKV50H2.0/德國朗盛/物性表參數

返回首頁返回物性參數列表