德國朗盛Durethan PA66 AKV30GHR是一種加30%玻璃纖維p66, 注塑成型，熱老化穩定，表面光潔度提高尼龍樹脂,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一系列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。

PA66 AKV30GHR物性表參數PDF文檔下載

生產商：LANXESS(德國朗盛)、品名：Durethan
PA66(尼龍66)AKV30GHR/德國朗盛/物性表參數

C	These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
C	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.64
C	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.82
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.05
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.04
Mechanical properties (23 °C/50 % r. h.)
C	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	8500	5600
C	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	135	90
C	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.2	6.5
C	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	70	65
C	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	55
C	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	<10
C	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	60	60
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	45
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	<10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	8000	5600
	Flexural strength	2 mm/min	MPa	ISO 178-A	215	150
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.8	5.8
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	210	130
C	Puncture maximum force	23 °C	N	ISO 6603-2	800
C	Puncture maximum force	-30 °C	N	ISO 6603-2	650
C	Puncture energy	23 °C	J	ISO 6603-2	2.5
C	Puncture energy	-30 °C	J	ISO 6603-2	2.0
Thermal properties
C	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	259
C	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	200
C	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	245
C	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	75
C	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.3
C	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
Other properties (23 °C)
C	Density		kg/m³	ISO 1183	1343
Processing conditions for test specimens
C	Injection molding-Melt temperature		°C	ISO 294	290
C	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120

德國朗盛Durethan PA66 AKV30GHR具有高抗震及抗裂性能，具體指標與材料的等級與含水量有關。彈性體改性的材料即使在低含水量及低溫下也具有良好的韌性,硬度高，尤其對于玻纖增強級別產品；拉伸模量：1,300 到 15,700 MPa (取決于含水量),良好的機械性能及阻尼吸聲效應、低摩擦力、急速運行能力好，氣體阻隔性能好（薄膜級）,

密度	1.01~1.23	模具溫度	80.0 到 100°C
加工（熔體）溫度	260 到 270°C	注射壓力	230 到 250°C
預熱	溫度/°C	130°C	工藝參數	注射時間	20~90
時間/h	4.0hr	高壓時間	0~5
料桶溫度/°C	后段	193 到 238°C	冷卻時間	20~90
中段	210 到 249°C	總周期	220 到 260°C
前段	221 到 254°C	螺桿轉數	30 到 60rpm
噴嘴溫度	232 到 274°C	使用注射機類型	螺桿式